Short Shot Injection Molding

Insufficient injection is also called short shot. Short shot is the phenomenon of partly incomplete at the end of the material flow, or a part of the cavity filled with dissatisfaction, especially the thin wall area or the end area of the the runner when injection molding. 

When the melt is cooled down without filling the mold cavity, or the melt does not fill completely after running into the cavity, it is called the short shot injection molding.

The main reason for short shot is that the flow resistance is too large, which makes the melt unable to continue to flow. The factors which impact the melt flow length including: 
* wall thickness of parts,
* mold temperature, 
* injection pressure, 
* melt temperature and material composition. 

If these factors are not handled properly, they will result in short shot.

​

Green Vitality Industry Co., Ltd offers high quality plastic injection molding services to meet the injection molding needs of any customer. We are engaged in a variety of industries mold and injection molding parts for more than 25 years.​

标签：

评论

发表评论

此博客中的热门博文

The polishing treatment methods for alumina ceramics

  It has become very common for thick film integrated circuits to use   alumina ceramics . Ceramic materials mainly made of alumina (Al2O3) have good conductivity, mechanical strength and high temperature resistance. It is a widely used ceramic at present. ​ However, after the alumina ceramic is sintered and cooled, it does not mean the end of product processing. Some products do not meet the application requirements. Therefore, they need to be processed, such as size correction and polishing. The polishing treatment method of alumina ceramics is as follows: 1. Using laser processing and ultrasonic processing for grinding and polishing. 2. Use Al2O3 powder or diamond paste for grinding and polishing. 3. The method of glazing is required (suitable for products that require high surface smoothness). 4. Use diamond, silicon carbide, etc. harder than alumina to grind step by step from coarse to fine. 5. The surface of the material is processed by ion implantation. Ion implantation...
发表评论
阅读全文

The solution of bubble issue during injection molding process

  According to the causes of bubbles, the countermeasures are as follows: (1) When the wall thickness of the product is large, the cooling speed of its external surface is faster than that of the central plastic part. Therefore, as the cooling goes on, the resin at the central part shrinks and expands towards the surface, resulting in insufficient filling at the central part. This condition is called a vacuum bubble. Solutions mainly include: A) Determine the reasonable gate and gate size according to the wall thickness. Generally, gate height shall be 50% ~ 60% of the wall thickness of the product. B) Until the gate is sealed, a certain amount of supplementary injection material is left. C) The injection time should be slightly longer than the gate sealing time. D) Reduce the injection speed and increase the injection pressure; E) Use materials with high melt viscosity. 2) The bubbles caused by the production of volatile gases are mainly solved as follows: A) Sufficient pre-drying...
发表评论
阅读全文

The application range of sandblasting treatment

Sandblasting is the process of cleaning and roughening the substrate surface by the impact of high-speed sand flow. Use compressed air as the power to form a high-speed jet beam to spray the blasting material (copper ore, quartz sand, corundum, iron sand, Hainan sand) at high speed on the surface of the workpiece to be processed, so that the appearance or shape of the outer surface of the workpiece surface changes. (1)  Workpiece coating and sandblasting before workpiece bonding can remove all dirt such as rust on the surface of the workpiece, and establish a very important basic pattern on the surface of the workpiece (the so-called rough surface). By changing the abrasives with different particle sizes, the roughness of different degrees is achieved, which greatly improves the binding force of the workpiece with coatings and plating materials. Or make the adhesive bond more firm and better quality. (2)  The rough surface of the casting, the cleaning and polishing of t...
发表评论
阅读全文